347H Hot Rolled Stainless Steel Plate No.1 Finish Niobium Stabilized Creep Resistant 3.0mm-50mm
Basic Properties
Place of Origin:
Shaanxi, China
Brand Name:
XYF
Certification:
ISO 9001:2015, SGS
Model Number:
347H-HR-No1
Trading Properties
Minimum Order Quantity:
5 Tons
Price:
USD 1200-3500 / Ton
Payment Terms:
T/T, L/C, Western Union
Supply Ability:
5000 Tons per Month
Product Summary
347H hot rolled stainless steel plate No.1 finish, niobium stabilized with high carbon for superior creep strength above 550°C.
Product Details
Highlight:
347H stainless steel plate
,hot rolled stainless steel plate
,niobium stabilized steel plate
Grade:
347H (UNS S34709)
Thickness:
3.0 - 50mm
Width:
1000/1500/2000mm
Length:
2000/3000/6000mm
Surface Finish:
No.1
Standard:
ASTM A240 / A480
Service Temperature:
550 - 800°C
Edge:
Sheared / Plasma Cut
Product Description
347H Hot Rolled Stainless Steel Plate No.1 Finish Niobium Stabilized Creep Resistant 3.0mm-50mm
347H hot rolled stainless steel plate is stabilized with niobium and specified with a higher carbon range (0.04-0.10%), providing excellent creep and stress rupture strength at temperatures above 550°C. It resists sensitization and intergranular attack after welding.
The No.1 finish suits heavy weld fabrication of high temperature equipment including superheater components and refinery heater parts.
Product Specifications
| Specification | Detail |
|---|---|
| Thickness | 3.0 - 50mm |
| Width | 1000mm / 1500mm / 2000mm |
| Length | 2000mm / 3000mm / 6000mm |
| Finish | No.1 (Hot Rolled Annealed Pickled) |
| Standard | ASTM A240, ASTM A480 |
| Service Temperature | 550 - 800°C |
| Edge | Sheared / Plasma cut |
| Tolerance | Thickness ±0.3mm, Width +20/-0mm |
Chemical Composition
| Element | Weight % |
|---|---|
| Carbon (C) | 0.04 - 0.10 |
| Manganese (Mn) | ≤ 2.00 |
| Phosphorus (P) | ≤ 0.045 |
| Sulfur (S) | ≤ 0.030 |
| Silicon (Si) | ≤ 1.00 |
| Chromium (Cr) | 17.0 - 19.0 |
| Nickel (Ni) | 9.0 - 13.0 |
| Niobium (Nb) | 8 x C - 1.00 |
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | ≥ 515 MPa |
| Yield Strength (0.2% offset) | ≥ 205 MPa |
| Elongation | ≥ 40% |
| Hardness | ≤ 95 HRB / ≤ 217 HBW |
Application Areas
- Superheater and reheater tubes
- Refinery heater components
- Thermal power station equipment
- High temperature fasteners
Mrs. Zhongcheng Metal
Manager
- Email: zhongcheng@metalsstainlesssteel.com
- Tel: 13309216881
- WhatsApp: 13309216881
-
WeChat:
13363905196
Related Products
-
309S Hot Rolled Stainless Steel Plate No.1 Finish Oxidation Resistant 3.0mm-60mm Heat Resistant
309S hot rolled stainless steel plate No.1 finish, high chromium nickel grade for oxidation resistance up to 1000°C. -
304L Hot Rolled Stainless Steel Plate No.1 Finish Low Carbon 3.0mm-100mm Weldable Structural
304L hot rolled stainless steel plate No.1 finish, low carbon grade 3.0-100mm, excellent weldability for tanks and structures. -
347H Hot Rolled Stainless Steel Plate No.1 Finish Niobium Stabilized Creep Resistant 3.0mm-50mm
347H hot rolled stainless steel plate No.1 finish, niobium stabilized with high carbon for superior creep strength above 550°C. -
317L Hot Rolled Stainless Steel Plate No.1 Finish High Molybdenum 3.0mm-80mm Chemical Processing
317L hot rolled stainless steel plate No.1 finish, high molybdenum 3-4%, superior pitting resistance for chemical processing.